alloy hot forging Forged round Steel bar shaft(4140 SCM440)
1.4140 42CrMo SCM440 steel rod Chemical Composition (%):
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
| 42CrMo4 |
0.38-0.45 |
0.17-0.37 |
0.40-0.70 |
≤0.035 |
≤0.035 |
0.90-1.20 |
0.15-0.25 |
| 1.7225 |
0.38-0.45 |
≤0.40 |
0.60-0.90 |
≤0.025 |
≤0.035 |
0.90-1.20 |
0.15-0.30 |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0.035 |
≤0.040 |
0.80-1.10 |
0.15-0.25 |
2.4140 alloy steel bar avaliable sizes
| Commodity delivery condition |
Dimensions |
| Hot rolled steel round bars |
10mm to 350mm |
| Forged steel round bars |
200mm to 800mm |
| Forged steel square block |
200mm*200mm to 500mm*500mm |
| Forged steel flat block |
(150mm to 500mm)*(200mm to 500mm) |
| Hot rolled and peeled or turned steel bright bars |
20mm to 800mm |
3.42CrMo4 steel bar delivery condition:
Hot rolled or forged, Peeled or black surface, annealed or QT.
4.4140 SCM440 steel bar applications:
Statically and dynamically stressed components for vehicles, engines and machines. For parts of larger cross-sections, crankshafts, gears.
5.1.7225 42CrMo4 steel round bar heat treatment:
Soft annealing: heat to 680-720°C, cool slowly.
Hardness after annealing: Max. 241 HB
Hardening: 820 - 850 °C
Normalizing temperature: 840-880°C
Tempering: 540-680°C
6.SCM400 4140 steel bar inspection:
Spectral Tested, Microstructure Tested,Hardness Test,Macrostructure Test,Ultrasonic according to the test standards:SEP1921-84,GR.3 CLASS C/C
7.Steel bar packing situation:
standard seaworthy packing or as customer required
8. 4140 steel bar delivery time:
always ready stock shipped within 7days,30 days for new material
9. 42CrMo4 alloy steel bar production process:
EAF+LF+VD ( necessary) +UT+ Peeled(optional) +Turned (optional) + Heat Treatment (optional)