Wear Resistant Steel plate
Abrasion Resisant Plate AR400 AR500
Abrasive resistant steel
Hard steel plate
hard 500 hard 400
steel plate cutting and bending
Product Descrition
1.Production Process
1)Steelmaking process Flow Chart
Blast Furance+Hot Metal Ladle Truck+KR Hot Metal Treatment+Converter+LF Refining Furnace+RH Vacuum Degassing Furance+Con-cast
2.Rolling Process Flow Chart
Reheating Furance+High-pressure Water Descaling+Edger Mill+Roughing Mill+Finishing Mill+Accelerated cooling+Hot Leveler+Marking and Spray Printing+Cooling Bed+On-line UT+Crop Shear+Double-side Trimming Shear+Cut-to-length Shear+Measurement+Marking and Spray Printing+Cold Leveler/Heat treatment
3.Heat-Treatment Flow Chart
Plate+Shot Blasting+Quenching Furance+Quenching Machine+Tempering Furance+Warm Leveler+Cooling Bed+Cutting+Cold Leveler+Finishing&Packaging
4.Thickness and Width
Thickness:4.5mm-150mm
Width:1600mm-4100mm
5.Main Grade
Germany:XAR400,XAR450,XAR500,XAR600,Dillidur400,Dillidur500
Belgium:QUARD400,QUARD450,QUARD500
France:FORA400,FORA500,Creusabro4800,Creusabro8000
Baosteel:B-HARD360,B-HARD400,B-HARD450,B-HARD500
HBIS:NM360,NM400,NM450,NM500
Finland:RAEX400,RAEX450,RAEX500
Japan:JFE-EH360,JFE-EH400,JFE-EH500,WEL-HARD400,WEL-HARD500
6.Application:
Crusher,sieve plate,feeding hopper,blade plate,conveyor,bucket,cutting edge,dump truck,scraper,industrial truck,railway wagon,bulldozer,excavator,screw conveyor and etc.
wear resistant steel plate NM400 property
| Chemical Composition |
steel plate |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
| Thicness |
% |
% |
% |
% |
% |
% |
% |
| 2-120mm |
0.11-0.20 |
0.38-0.55 |
1.20-1.55 |
0.005-0.020 |
0.005-0.010 |
0.01-0.60 |
0.004-0.04 |
| Hardness |
370-430HB |
| Michanical Properties |
10mm thickness steel plate typical value |
Yiled Strength |
Tebsile Strength |
Elongation |
| Re |
Rm |
A5 |
| Mpa |
Mpa |
% |
| >1050 |
>1250 |
12 |
| Impact Toughness |
10mm thickness steel plate typical value |
Test |
Impact test |
| Temperature |
Charpy-V Longitudinal |
| ºC |
J |
| -20 |
40 |
wear resistant steel plate NM450 property
| Chemical Composition |
steel plate |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
| Thicness |
% |
% |
% |
% |
% |
% |
% |
| 2-120mm |
0.20-0.26 |
0.75-0.95 |
1.60-1.80 |
0.015-0.020 |
0.005-0.010 |
0.01-0.60 |
0.001-0.04 |
| Hardness |
420-480HB |
| Michanical Properties |
10mm thickness steel plate typical value |
Yiled Strength |
Tebsile Strength |
Elongation |
| Re |
Rm |
A5 |
| Mpa |
Mpa |
% |
| >1150 |
>1300 |
10 |
| Impact Toughness |
10mm thickness steel plate typical value |
Test |
Impact test |
| Temperature |
Charpy-V Longitudinal |
| ºC |
J |
| -20 |
30 |
Application:Sieve plate,wear resistant liner,feeding hopper,powder concentrator,conveyor,scraper conveyor,dump truck,screw conveyor and etc.
| Chemical Composition |
steel plate |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
| Thicness |
% |
% |
% |
% |
% |
% |
% |
| 2-120mm |
0.25-0.35 |
0.25-1.75 |
0.40-1.60 |
0.015-0.020 |
0.005-0.010 |
0.20-0.80 |
0.001-0.03 |
| Hardness |
470-530HB |
| Michanical Properties |
10mm thickness steel plate typical value |
Yiled Strength |
Tebsile Strength |
Elongation |
| Re |
Rm |
A5 |
| Mpa |
Mpa |
% |
| >1250 |
>1500 |
8 |
| Impact Toughness |
10mm thickness steel plate typical value |
Test |
Impact test |
| Temperature |
Charpy-V Longitudinal |
| ºC |
J |
| -20 |
20 |
Application:Wear resistant strip,chute,sieve plate,knives,cutting edge and etc.
NM550
| Chemical Composition |
steel plate |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
| Thicness |
% |
% |
% |
% |
% |
% |
% |
| 2-120mm |
0.30-0.37 |
0.2-0.405 |
0.40-1.60 |
0.010-0.020 |
0.005-0.010 |
0.30-0.80 |
0.002-0.60 |
| Hardness |
520-580HB |
| Michanical Properties |
10mm thickness steel plate typical value |
Yiled Strength |
Tebsile Strength |
Elongation |
| Re |
Rm |
A5 |
| Mpa |
Mpa |
% |
| >1300 |
>1550 |
6 |
| Impact Toughness |
10mm thickness steel plate typical value |
Test |
Impact test |
| Temperature |
Charpy-V Longitudinal |
| ºC |
J |
| -20 |
12 |
Application:Wear resitant strip,chute,sieve plate,cutting edge and etc.
NM600
| Chemical Composition |
steel plate |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
| Thicness |
% |
% |
% |
% |
% |
% |
% |
| 2-120mm |
0.35-0.40 |
0.20-0.80 |
0.40-1.60 |
0.010-0.020 |
0.005-0.010 |
0.25-1.00 |
0.002-0.60 |
| Hardness |
560-620HB |
| Michanical Properties |
10mm thickness steel plate typical value |
Yiled Strength |
Tebsile Strength |
Elongation |
| Re |
Rm |
A5 |
| Mpa |
Mpa |
% |
| >1450 |
>1650 |
5 |
| Impact Toughness |
10mm thickness steel plate typical value |
Test |
Impact test |
| Temperature |
Charpy-V Longitudinal |
| ºC |
J |
| -20 |
8 |
NM650
| Chemical Composition |
steel plate |
C |
Si |
Mn |
P |
S |
Cr |
Ni |
| Thicness |
% |
% |
% |
% |
% |
% |
% |
| 2-120mm |
0.40-0.50 |
0.20-0.80 |
0.40-1.60 |
0.010-0.020 |
0.005-0.010 |
0.80-1.50 |
0.002-0.60 |
| Hardness |
620-680HB |
| Michanical Properties |
10mm thickness steel plate typical value |
Yiled Strength |
Tebsile Strength |
Elongation |
| Re |
Rm |
A5 |
| Mpa |
Mpa |
% |
| >1500 |
>1750 |
3 |
| Impact Toughness |
10mm thickness steel plate typical value |
Test |
Impact test |
| Temperature |
Charpy-V Longitudinal |
| ºC |
J |
| -20 |
6 |
We have CNC flame,underwater plasma,Laser cutting machine,3600tons of bending machine,1600tons,1000tons of press machine,veneer reeling machine,CNC machine center,drilling machine,wire cutting and other advanced large cutting machining equipment.
Our CNC cutting equipment
CNC Flame Cutting machine
Effective cutting length:20000mm
Effective cutting width:5000mm
Max cutting thickness:120mm
Cutting precision:+/-2mm
Cutting speed:50--6000mm/min
CNC plasma cutting machine underwater
Effective cutting length:17000mm
Effective cutting width:5000mm
Max cutting thickness:30mm
Cutting precision:+/-1mm
Cutting speed:50--6000mm/min
CNC Laser cutting machine
Effective cutting length:20000mm
Effective cutting width:5000mm
Max cutting thickness:20mm
Cutting precision:+/-0.2mm
Cutting speed:50--6000mm/min
CNC Bending equipment
3600tons of bending machine
Max bending length:12200mm
Max bending width:4400mm
Bending angle:<90 degree